Measures of Avoid 3 PE Coating Pipe End Become Warped Edge

Views: 2     Author: Site Editor     Publish Time: 2023-06-14      Origin: Site

1, In the condition of not effect the process of pipe welding, should be appropriate to increase the reserved length, epoxy powder end of polyethylene layer can be prevented because of steel pipe pile up for a long time, pipe metal corrosion caused by severe 3 PE anticorrosive become warped edge.

2, Anticorrosive pipe for a long time, deposited in the open air shall be covered in the pipe, prevent the rain erosion, causing severe corrosion pipe end.

3, If the pipeline field construction cycle is long, can besmear brushs weldable anti-rust paint tube bare metal, to prevent corrosion pipe caused by corrosion during storage of 3 PE coating become warped edge.

More than 4, strict control of tube end reserved in weld grinding with high quality. Polyethylene in weld slope outlets and the rest of the pipe body, make the epoxy powder reserved length > 20 mm, in order to prevent the welds epoxy powder at the bottom of the corrosion caused by the first 3 PE anticorrosion layer become warped edge.

Related Products

content is empty!

Hunan Great Steel Pipe Co.,Ltd
Hunan Great Steel Pipe Co.,Ltd is a world-class production and service provider of submerged arc straight seam welded pipe as the first subsidiary of Shinestar Group. Hunan Great Steel Pipe Co.,Ltd pays more attention to in the pipeline engineering research areas as a pioneer of China Petroleum Pipeline & Gas Pipeline Science Research Institute.



 Tel: +86-0731-88672086 
 Address: Hunan Steel Industrial Zone,No.9 Xiangfu Road, Yuhua District, Changsha,    Hunan, China
Copyright © Hunan Great Steel Pipe Co.,Ltd. All Rights Reserved. Sitemap